Based on the accumulated clinical cases and studies over 10 years, IS-II active has been continuously developed for the improvement. IS-II active has an internal submerged type design with S.L.A. surface that allows faster and stronger osseointegration.

S.L.A. surface is formed by undergoing the process of sandblasting with smaller than 50㎛ HA (Hydroxy Apatite) particles to roughen the machined surface and to form many macropores. After sandblastingand acid

etching is done to increase B.I.C. and promote cell’s activity. With this process, the typical treatment period

can be shortened and the patients will be more satisfied with the result.

It is observed that S.L.A. surface has the capability of attaching more cells on the titanium surface than the machined or R.B.M. surfaces.

Measured distance of newly formed bone is approved to be longer in S.L.A. surface compared to R.B.M. surface.

S.L.A. Surface has no impurities on the implant surface (No residual acid or cell toxicity

is observed in the material examination). Also it has an appropriate rough average that

can have the excellent osteoconductivity.

BioSeal has a curved S shape with the application of 0.5mm micro grooves on the machined surface.

This design is invented to minimize the bone loss by maximizing soft tissue sealing

Coronal macro threads helps to achieve excellent primary stability at the cortical bone and initial

fixation at the apex is excellent, therefore IS-II active works great in both immediate placement and

immediate loading.

Magic Thread with the inverted triangular shaped powerful deep thread helps to achieve strong and

stable initial f ixation and also this special design allows to endure vertical and lateral forces effectively

Apex is powerful in drilling and due to this selfcompactable and tapered apex design, initial

fixation is easily achieved. It works great in both

immediate placement and immediate loading.

Regular, Wide 7.3mm Fixture

Wide 8.5, 10.0, 11.5, 13.0mm Fixture